ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 发泡 其它 | 外观颜色 | |
| 该料用途 | 鞋底发泡挤压，薄膜挤压 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 其它性能 | 薄膜 | MD | ASTM D-638/D-882 | 480 | % | |
| TD | ASTM D-638/D-882 | 640 | % | |||
| 基本性能 | 密度 | ASTM D-1505 | 0.942 | g/cm3 | ||
| 机械性能 | 冲击强度 | ASTM D-1709 | 374 | G/F50 | ||
| 其它性能 | 铸膜成型 | ASTM D-638/D-882 | 180 | kg/cm2 | ||
| 硬度 | ASTM D-2240 | 36 | Shore D | |||
| 低温易脆性 | ASTM D-746 | <-76 | ℃/F50 | |||
| 射出 | ASTM D-638/D-882 | 250 | % | |||
| VA含量 | ASTM USIFE | 22 | % | |||
| 薄膜 | MD | ASTM D-638/D-882 | 264 | kg/cm2 | ||
| TD | ASTM D-638/D-882 | 189 | kg/cm2 | |||
| 熔融指数 | ASTM D-1238 | 1.4 | g/10min | |||
| VICAT 软化点 | ASTM D-1525 | 64 | ℃ | |||
| 融化点 | ASTM D-2117 | 82 | ℃ | |||
| 射出 | ASTM D-638/D-882 | 110 | kg/cm2 | |||
| 铸膜成型 | ASTM D-638/D-882 | 800 | % | |||