ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 硬度 | ShoreA/D | ASTM D2240 | 65A | |
| 密度 | ASTM D792 | 0.95 | g/cm³ | ||
| 机械性能 | 拉伸强度 | ASTM D412 | 6.0 | MPa | |
| 断裂伸长率 | ASTM D412 | 450 | % | ||
| 撕裂强度 | ASTM D624 | 32.5 | KN/M | ||
| 压缩形变 | 22h/70℃ | ASTM D395 | 44 | % | |
| 脆化温度 | ASTM D746 | -60 | ℃ | ||
| 热性能 | 热空气老化，100℃/168h | 硬度，5S | ASTM D2240 | 67A | |
| 拉伸强度保持率 | ASTM D412 | 93 | |||
| 断裂伸长保持率 | ASTM D412 | 92 | |||
| 热空气老化，135℃/72h | 硬度，5S | ASTM D2240 | 68A | ||
| 拉伸强度保持率 | ASTM D412 | 91 | |||
| 断裂伸长保持率 | ASTM D412 | 90 | |||
| 耐臭氧老化试验，100ppm/40℃/96h | ASTM D1119 | 无裂纹 | |||
| 氙灯老化试验，65℃＞2000h 8KJ/M | 拉伸强度保持率 | ASTM D412 | 92 | ||
| 断裂伸长保持率 | ASTM D412 | 92 | |||
| 电气性能 | 介电常数 | ASTM D150 | 2.35 | ||
| 20℃，体积电阻率 | ASTM D257 | 1.6E+14 | |||
| 70℃，体积电阻率 | ASTM D257 | 1.1E+12 | |||
| 95℃，体积电阻率 | ASTM D257 | 1.0E+12 | |||
| 其它 | 耐油性，125℃/70h 3# | ASTM D471 | 55 | ||
| 燃烧性能 | ISO 3795 | ＜100 | |||