ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.947 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 6.0 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
20 |
µm
|
|
| 膜刺穿性 | 20 µm | Internal Method | 0.485 |
J/cm³
|
|
|
割线模量
|
TD : 20 µ | ASTM D882 | 512 |
MPa
|
|
|
1% 正割, TD : 20 µm
|
ASTM D882 | 428 |
MPa
|
||
|
2% 正割, TD : 20 µm
|
ASTM D882 | 327 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 20 µm
|
ASTM D882 | 15.1 |
MPa
|
|
|
TD : 屈服, 20 µm
|
ASTM D882 | 15.1 |
MPa
|
||
|
MD : 断裂, 20 µm
|
ASTM D882 | 12.0 |
MPa
|
||
|
TD : 断裂, 20 µm
|
ASTM D882 | 10.3 |
MPa
|
||
|
伸长率
|
MD : 屈服, 20 µm
|
ASTM D882ASTM D882 | 9.7 | % | |
|
TD : 屈服, 20 µm
|
6.3 | % | |||
|
|
MD : 断裂, 20 µm
|
ASTM D882 | 260 | % | |
|
TD : 断裂, 20 µm
|
ASTM D882 | 85 | % | ||
| 落锤冲击 | 20 µm | ASTM D1709 | 52 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 20 µm
|
ASTM D1922 | 43 |
g
|
|
|
TD : 20 µm
|
ASTM D1922 | 84 |
g
|
||