ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.917 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 1.3 |
g/10 min
|
|
| 薄膜 | 薄膜厚度 |
经测试
|
25 |
µm
|
|
| 膜刺穿强度 | Internal Method | 4.96 |
J
|
||
|
膜刺穿力
|
Internal Method | 56.8 |
N
|
||
|
膜耐刺穿性
|
Internal Method | 22.5 |
J/cm³
|
||
|
膜强度
|
MD
|
ASTM D882 | 94.6 |
J/cm³
|
|
| TD | ASTM D882 | 92.1 |
J/cm³
|
||
|
割线模量
|
1% 正割, MD
|
ASTM D882 | 185 |
MPa
|
|
|
2% 正割, MD
|
ASTM D882 | 154 |
MPa
|
||
|
1% 正割, TD
|
ASTM D882 | 219 |
MPa
|
||
|
2% 正割, TD
|
ASTM D882 | 185 |
MPa
|
||
|
抗张强度
|
MD : 屈服
|
ASTM D882 | 11.1 |
MPa
|
|
|
TD : 屈服
|
ASTM D882 | 11.0 |
MPa
|
||
|
MD : 断裂
|
ASTM D882 | 44.3 |
MPa
|
||
|
TD : 断裂
|
ASTM D882 | 34.6 |
MPa
|
||
|
伸长率
|
MD : 断裂
|
ASTM D882 | 510 | % | |
|
TD : 断裂
|
ASTM D882 | 590 | % | ||
| 落锤冲击 | ASTM D1709 | 400 |
g
|
||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 450 |
g
|
|
|
TD
|
ASTM D1922 | 590 |
g
|
||
| 热性能 | 溶融温度 | DSC | Internal Method | 118 | ℃ |
| 光学性能 | 光泽度 | 45° | ASTM D2457 | 64 | |
| 雾度 | ASTM D1003 | 7.5 | % | ||