ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 吹塑,挤出 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.920 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ISO 1133 | 2.0 |
g/10 min
|
|
| 薄膜 |
薄膜厚度
|
经测试 | 51 |
µm
|
|
| 膜耐刺穿性 | Internal Method | 2.90 |
J/cm³
|
||
|
膜强度
|
MD : 51 µm
|
ASTM D882 | 159 |
J/cm³
|
|
|
TD : 51 µm
|
ASTM D882 | 185 |
J/cm³
|
||
|
割线模量
|
2% 正割, MD : 51 µm
|
ASTM D882 | 181 |
MPa
|
|
|
2% 正割, TD : 51 µm
|
ASTM D882 | 207 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 51 µm
|
ASTM D882 | 12.3 |
MPa
|
|
|
TD : 屈服, 51 µm
|
ASTM D882 | 12.1 |
MPa
|
||
|
MD : 断裂, 51 µm
|
ASTM D882 | 24.8 |
MPa
|
||
|
TD : 断裂, 51 µm
|
ASTM D882 | 23.0 |
MPa
|
||
|
伸长率
|
MD : 断裂, 51 µm
|
ASTM D882 | 420 | % | |
|
TD : 断裂, 51 µm
|
ASTM D882 | 670 | % | ||
| 落锤冲击 | 51 µm | ASTM D1709A | 150 |
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 51 µm
|
ASTM D1922 | 500 |
g
|
|
|
TD : 51 µm
|
ASTM D1922 | 280 |
g
|
||
| 热性能 |
维卡软化温度
|
ASTM D1525 | 98.3 | ℃ | |
| 溶融温度 | DSC | Internal Method | 112 | ℃ | |
| 光学性能 | 光泽度 | 45°, 50.8 µm | ASTM D2457 | 66 | |
| 雾度 | 50.8 µm | ASTM D1003 | 7.6 | % | |