ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃/5kg | ASTM D-1238 | 5.5 | g/10min |
| 熔体流动速率 | 230℃/3.8kg | ASTM D-1238 | 10.0 | g/10min | |
| 吸水率 | 24hr | ASTM D-570 | 0.3 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.07 | g/cm3 | |
| 模具收缩率 | Flow | ASTM D-955 | 0.2-0.6 | % | |
| 机械性能 | 拉伸强度 | ASTM D-638 | 620 | kg/cm2 | |
| 断裂伸长率 | ASTM D-638 | 4.5 | % | ||
| 弯曲模量 | ASTM D-790 | 33600 | kg/cm2 | ||
| 弯曲强度 | ASTM D-790 | 900 | kg/cm2 | ||
| IZOD缺口冲击强度 | 3.2mm | ASTM D-256 | 1.5 | J/m | |
| 洛氏硬度 | ASTM D-785 | 82 | M scale | ||
| 热性能 | 热变形温度 | 18.6kg/cm2，未退火 | ASTM D-648 | 90 | ℃ |
| 维卡软化温度 | 1kg,50℃/h | ASTM D-1525 | 107 | ℃ | |
| 燃烧性 | 1.6mm | UL 94 | HB | ||