ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.939 |
g/cm³
|
|
|
熔流率
|
190℃/2.16 kg
|
ASTM D1238 | 0.60 |
g/10 min
|
|
|
190℃/2.16 kg
|
ASTM D1238 | 40 |
g/10 min
|
||
| 抗环境应力开裂 | F0 | ASTM D1693C |
> 2000
|
hr
|
|
| 50°C, 100% Igepal, F50 | ASTM D1693 |
> 1500
|
hr
|
||
|
硬度计硬度
|
邵氏 D | ASTM D2240 | 56 | ||
| 邵氏 D | ASTM D2240 | 61 | |||
| 机械性能 |
抗张强度
|
屈服
|
ASTM D638 | 19.0 |
MPa
|
| 屈服 | ASTM D638 | 20.0 |
MPa
|
||
|
断裂
|
ASTM D638 | 20.7 |
MPa
|
||
| 断裂 | ASTM D638 | 21.4 |
MPa
|
||
|
伸长率
|
屈服
|
ASTM D638 | 4.0 | % | |
| 断裂 | ASTM D638 |
> 800
|
%
|
||
|
断裂
|
ASTM D638 | 700 | % | ||
| 弯曲模量 |
-
|
ASTM D790B | 655 |
MPa
|
|
| 2% 正割 | ASTM D790B | 600 |
MPa
|
||
| 拉伸冲击强度 | ASTM D1822 | 231 |
kJ/m²
|
||
|
热性能 |
热变形温度 | 0.45 MPa, 未退火 | ASTM D648 | 55.0 | ℃ |
|
脆化温度
|
-- | ASTM D746A |
< -95.0
|
℃ | |
| -- | ASTM D746 |
< -76.1
|
℃ | ||
|
维卡软化温度
|
ASTM D1525 | 120 | ℃ | ||
| 溶融温度 | DSC | Internal Method | 126 | ℃ | |
| 结晶峰温 | DSC | Internal Method | 115 | ℃ | |