ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
ASTM D792 | 0.902 |
g/cm³
|
|
| 熔流率 | 190℃/2.16 kg | ASTM D1238 | 3.0 |
g/10 min
|
|
| 薄膜 |
薄膜厚度
|
经测试 | 20 |
µm
|
|
| 膜刺穿强度 | 20 µm | Internal Method | 4.28 |
J
|
|
| 膜刺穿力 | 20µm | Internal Method | 47.6 |
N
|
|
| 膜耐刺穿性 | 20 µm | Internal Method | 31.4 |
J/cm³
|
|
|
割线模量
|
2% 正割, MD : 20µm
|
ASTM D882 | 108 |
MPa
|
|
|
2% 正割, TD : 20µm
|
ASTM D882 | 115 |
MPa
|
||
|
抗张强度
|
MD : 屈服, 20 µm
|
ASTM D882 | 9.93 |
MPa
|
|
|
TD : 屈服, 20 µm
|
ASTM D882 | 5.45 |
MPa
|
||
|
MD : 断裂,20µm
|
ASTM D882 | 44.6 |
MPa
|
||
|
TD : 断裂,20µm
|
ASTM D882 | 29.8 |
MPa
|
||
| 伸长率 |
MD : 断裂, 20 µm
|
ASTM D882 | 350 | % | |
|
TD : 断裂, 20µm
|
ASTM D882 | 570 | % | ||
| 落锤冲击 | 20 µm | ASTM D1709B |
> 830
|
g
|
|
| 埃尔曼多夫抗撕强度 |
MD : 20µm
|
ASTM D1922 | 120 |
g
|
|
|
TD : 20µm
|
ASTM D1922 | 410 |
g
|
||
| 始封温度 | 20 µm | Internal Method | 93.9 | ℃ | |
| 热性能 |
维卡软化温度
|
ASTM D1525 | 85.0 | ℃ | |
| 溶融温度 | DSC | Internal Method | 98.0 | ℃ | |
| 光学性能 | 光泽度 | 20°, 20.3 µm | ASTM D2457 | 144 | |
| 雾度 |
20.3µm
|
ASTM D1003 | 0.70 | % | |