ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
|
物理性能 |
收缩率 |
流动: 150°C, 30分钟, 0.0100 mm | ASTM D1204 | 2.5 | % |
|
流动: 150°C, 30分钟, 0.0120 mm
|
ASTM D1204 | 2.5 | % | ||
| 横向流动: 150°C, 30分钟, 0.0100 mm | ASTM D1204 | 0.4 | % | ||
| 横向流动: 150°C, 30分钟, 0.0120 mm | ASTM D1204 | 0.4 | % | ||
| 表面张力 | Metallized side (10.0 µm) | ASTM D2578 |
56
|
dyne/cm
|
|
| Metallized side (12.0 µm) | ASTM D2578 | 56 |
dyne/cm
|
||
|
薄膜 |
薄膜厚度 - 经测试 | 10,12 | µm | ||
| 可供应的薄膜厚度 | 10,12 | µm | |||
|
抗张强度 |
MD: 断裂, 10 µm | ASTM D882 | 206 | MPa | |
| MD: 断裂, 12 µm | ASTM D882 | 206 | MPa | ||
| TD: 断裂, 10µm | ASTM D882 | 216 | MPa | ||
| TD: 断裂, 12 µm | ASTM D882 | 216 | MPa | ||
| 伸长率 | MD: 断裂, 10 µm | ASTM D882 | 100 | % | |
| MD: 断裂, 12 µm | ASTM D882 | 100 | % | ||
| TD: 断裂, 10 µm | ASTM D882 | 90 | % | ||
| TD: 断裂, 12 µm | ASTM D882 | 90 | % | ||
| 透氧率 | (23°C, 10 µm) | ASTM D3985 |
0.700
|
cm³/m²/24 hr
|
|
| (23°C, 12 µm) | ASTM D3985 |
0.800
|
cm³/m²/24 hr
|
||
| 用量 | 10.0 µm | Internal Method | 71.4 | m²/kg | |
| 12.0 µm | Internal Method | 59.5 | m²/kg | ||
|
|
水蒸气透过性 |
37.8°C, 90%RH, 10 µm
|
ASTM F1249 |
0.40
|
g/m²/24 hr
|
| 37.8°C, 90%RH, 12 µm | ASTM F1249 |
0.50
|
g/m²/24 hr
|
||
|
Optical Density
|
10.0 µm
|
Internal Method |
-2.4 到 7.6
|
% | |
|
12.0 µm
|
Internal Method |
-2.4 到 7.6
|
% | ||