ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 吹塑,挤出,注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重
|
--
|
ASTM D792 | 1.18 |
g/cm³
|
|
--
|
ISO 1183 | 1180 |
kg/m³
|
||
| 熔流率 | 330℃/2.16 kg | ASTM D1238, ISO 1133 | 26 |
g/10 min
|
|
| 熔体体积流动速率 | 330℃/2.16 kg | ISO 1133 | 25.0 |
cm³/10min
|
|
|
吸水率
|
23℃, 24 hr
|
ASTM D570 | 0.20 | % | |
|
饱和, 23℃
|
ASTM D570 | 0.40 | % | ||
|
饱和
|
ISO 62 | 0.40 | % | ||
|
平衡
|
ISO 62 | 0.20 | % | ||
|
球压硬度
|
ISO 2039-1 | 115 |
MPa
|
||
| 机械性能 |
拉伸模量
|
23℃ | ASTM D638 | 2280 |
MPa
|
| -- | ISO 527-2 | 2300 |
MPa
|
||
|
抗张强度
|
屈服, 23℃
|
ASTM D638 | 64.8 |
MPa
|
|
|
屈服
|
ISO 527-2 | 65.0 |
MPa
|
||
|
伸长率
|
屈服, 23℃
|
ASTM D638 | 7.0 | % | |
|
屈服
|
ISO 527-2 | 7.0 | % | ||
|
断裂, 23℃
|
ASTM D638 | 50 | % | ||
|
断裂伸长率
|
ISO 527-2 | >50 | % | ||
| 弯曲模量 | ISO 178 | 2200 |
MPa
|
||
| 弯曲强度 | ISO 178 | 95.0 |
MPa
|
||
|
简支梁缺口冲击强度
|
-30℃ | ISO 179/1eA | 10.0 |
kJ/m²
|
|
| 23℃ | ISO 179/1eA | 10.0 |
kJ/m²
|
||
|
简支梁冲击强度
|
-30℃ | ISO 179/1eU |
无断裂
|
||
| 23℃ | ISO 179/1eU |
无断裂
|
|||
|
无缺口悬臂梁冲击
|
-40℃, 3.18 mm
|
ASTM D256 |
无断裂
|
||
|
23℃, 3.18 mm
|
ASTM D256 |
无断裂
|
|||
| 热性能 |
热变形温度
|
0.45 MPa, 未退火, 6.35 mm
|
ASTM D648 | 152 | ℃ |
|
0.45 MPa
|
ISO 75-2 | 152 | ℃ | ||
|
1.8 MPa, 未退火, 6.35 mm
|
ASTM D648 | 140 | ℃ | ||
|
1.8 MPa, 退火
|
ISO 75-2/A | 157 | ℃ | ||
|
1.8 MPa
|
ISO 75-2 | 140 | ℃ | ||
|
维卡软化温度
|
-- | ASTM D1526, ISO 306/B120 | 160 | ℃ | |
|
50℃/h, B (50N)
|
ISO 306 | 158 | ℃ | ||
|
线形膨胀系数
|
流动
|
ASTM D696 | 0.000070 |
cm/cm/℃
|
|
|
横向
|
ISO 11359-2 | 0.000070 | cm/cm/℃ | ||
| 电气性能 |
表面电阻率
|
-- | ASTM D257 |
1.0E+16
|
ohm
|
| -- | IEC 60093 |
> 1.0E+15
|
ohm
|
||
|
体积电阻率
|
-- | ASTM D257 |
1.0E+18
|
ohm·cm
|
|
| -- | IEC 60093 |
> 1.0E+13
|
ohm·cm
|
||
|
介电强度
|
23℃, 3.18 mm, in Oil | ASTM D149 | 16 |
kV/mm
|
|
| -- | IEC 60243-1 | 35 |
kV/mm
|
||
|
介电常数
|
23℃, 60 Hz
|
ASTM D150 | 3.00 | ||
|
23℃, 1 MHz
|
ASTM D150 | 3.00 | |||
|
100 Hz
|
IEC 60250 | 3.00 | |||
|
1 MHz
|
IEC 60250 | 3.00 | |||
|
耗散因数
|
23℃, 60 Hz
|
ASTM D150 | 0.0010 | ||
|
23℃, 1 MHz
|
ASTM D150 | 0.010 | |||
|
100 Hz
|
IEC 60250 | 0.0016 | |||
|
1 MHz
|
IEC 60250 | 0.0087 | |||
|
漏电起痕指数
|
解决方案 | IEC 60112 | 100 |
V
|
|
| -- | IEC 60112 | 375 | |||
| 可燃性 |
UL 阻燃等级
|
1.50 mm
|
UL 94 |
HB
|
|
|
3.00 mm
|
UL 94 |
HB
|
|||
| 燃烧性能 正常厚度 1.6mm | 1.50 mm, UL | ISO 1210 |
HB
|
||
| 一定厚度与小时下的阻燃等级 | 3.00 mm, UL) | ISO 1210 |
HB
|
||
|
极限氧指数
|
ASTM D2863, ISO 4589-2 | 24 | % | ||
| 光学性能 |
折射率
|
-- | ASTM D542 | 1.581 | |
| -- | ISO 489 | 1.581 | |||
| 透射率 | 3180 µm | ASTM D1003 | 88.0 | % | |
| 雾度 | 3180 µm | ASTM D1003 | 1.0 | % | |