ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
熔流率
|
ASTM D1238 | 2.0 |
g/10 min
|
|
|
醋酸乙烯含量
|
|
18.0 |
wt%
|
||
| 硬度计硬度 | 支撐 A | ASTM D2240 | 91 | ||
| 机械性能 | 抗张强度 |
MD: 屈服
|
ASTM D882 | 40.0 |
MPa
|
|
TD: 屈服
|
ASTM D882 | 30.3 |
MPa
|
||
|
|
MD: 断裂
|
ASTM D882 | 4.68 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 4.30 |
MPa
|
||
| 伸长率 |
MD: 屈服
|
ASTM D882 | 410 | % | |
|
TD: 屈服
|
ASTM D882 | 560 | % | ||
|
MD: 断裂
|
ASTM D882 | 9.0 | % | ||
|
TD: 断裂
|
ASTM D882 | 9.0 | % | ||
|
落锤冲击
|
ASTM D1709A | 610 |
g
|
||
| 热性能 |
脆化温度
|
ASTM D746 |
< -76.0
|
℃ | |
|
维卡软化温度
|
ASTM D1525 | 65.0 | ℃ | ||