| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTM D792, ISO 1183 |
1.07 |
g/cm³
|
| |
溶化体积流率 |
MVR 220°C/10.0 kg
|
ASTM D1238 |
5.00 |
cm³/10min
|
| |
|
MVR 220°C/10.0 kg
|
ISO 1133 |
5.50 |
cm³/10min |
| |
收缩率 |
流动
|
ASTM D955 |
0.55 |
%
|
| |
吸水率 |
饱和, 23℃
|
ASTM D570 |
1.7 |
%
|
| 硬度 |
洛氏硬度 |
R 计秤 |
ASTM D785 |
90 |
|
| 机械性能 |
拉伸模量 |
23℃
|
ASTM D638 |
1830 |
MPa
|
| |
抗张强度 |
屈服, 23℃ |
ASTM D638 |
40.0 |
MPa
|
| |
伸长率 |
屈服, 23℃ |
ASTM D638 |
2.9 |
%
|
| |
弯曲模量 |
23℃ |
ASTM D790 |
1560 |
MPa
|
| |
弯曲强度 |
23℃ |
ASTM D790 |
57.0 |
MPa
|
| |
简支梁缺口冲击强度 |
-40℃ |
ASTM D256 |
57 |
J/m
|
| |
|
23℃ |
ASTM D256 |
280 |
J/m
|
| 热性能 |
热变形温度 |
1.8 MPa, 未退火
|
ASTM D648 |
82.0 |
℃ |
| |
维卡软化温度 |
|
ASTM D1525 3 |
90.0 |
℃ |
| |
线形膨胀系数 |
流动
|
ISO 11359-2 |
0.000095 |
cm/cm/℃ |
| 电气性能 |
表面电阻率 |
|
ASTM D257, IEC 60093 |
>1.0E+13
|
ohm
|
| |
体积电阻率 |
|
ASTM D257, IEC 60093 |
>1.0E+14
|
ohm·cm
|
| |
介电常数 |
1.00 mm, 1 MHz
|
ASTM D150 |
3.30 |
|
| |
|
|
IEC 60250 |
3.80 |
|
| |
|
1 MHz
|
IEC 60250 |
3.30 |
|
| |
耗散因数 |
100 Hz
|
IEC 60250 |
0.0090 |
|
| |
|
1 MHz
|
IEC 60250 |
0.026 |
|
| |
漏电起痕指数 |
|
IEC 60112 |
600 |
V
|
| |
耐电强度 |
|
IEC 60243-1 |
35 |
kV/mm
|
| 其他 |
Gardner光泽度 |
60° |
ASTM D523 |
91 |
|
|