ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：矿物增强30% | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 燃烧率 | UL94 | HB | ||
| 吸水率 | ASTM D-570 | 1.0 | % | ||
| 成型收缩率 | UBEmethod | 0.8 | % | ||
| 成型收缩率 | UBEmethod | 0.7 | % | ||
| 吸水率 | ASTM D-570 | 6.4 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.50 | ||
| 机械性能 | 断裂下的延伸率 | 23° | ASTM D-638 | 7 | % |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 300 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 20000 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 61000 | kgf/cm2 | |
| 熔点 | DSC | 215-225 | °C | ||
| 弯曲强度 | 23° | ASTM D-790 | 1500 | kgf/cm2 | |
| 挤剪强度 | 23° | ASTM D-732 | 720 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 90 | ||
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | ||
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 170 | kgf/cm2 | |
| 抗冲击强度 | -30° | ASTM D-256 | 3.5 | kgf.cm/cm | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 510 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 880 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 650 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 400 | kgf/cm2 | |
| 屈服下的伸张强 | -30° | ASTM D-638 | 1240 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 4.0 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 105 | ||
| 抗冲击强度 | 23° | ASTM D-256 | 14 | kgf.cm/cm | |
| 弯曲强度 | -30° | ASTM D-790 | 1850 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 抗冲击强度 | -30° | ASTM D-256 | 5.0 | kgf.cm/cm | |
| 断裂下的延伸率 | 23° | ASTM D-638 | 5 | % | |
| TABER磨耗率 | ASTM D-1044 | 20 | mg | ||
| 电气性能 | 绝缘耐力 | ASTM D-149 | 21 | KV/mm | |
| 介电常数 | 60HZ | ASTM D-150 | 4.4 | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.01 | ||
| 体积电阻率 | ASTM D-257 | 1012 | |||
| 抗电弧强度 | ASTM D-495 | 120 | S | ||
| IEC电路 | UL746 | 600+ | V | ||
| 介电常数 | 106HZ | ASTM D-150 | 4.0 | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介电常数 | 103HZ | ASTM D-150 | 4.3 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.01 | ||
| 体积电阻率 | ASTM D-257 | 1015 | |||
| 热性能 | 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 160 | °C |
| 线性热膨胀系数 | ASTM D-696 | 5 | X的10-5cm/cm/°C | ||
| 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 200 | °C | |