ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 特性：玻纤增强20% | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | ASTM D-570 | 1.3 | % | |
| 成型收缩率 | UBEmethod | 0.4 | % | ||
| 吸水率 | ASTM D-570 | 7.4 | % | ||
| 成型收缩率 | UBEmethod | 0.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.28 | ||
| 机械性能 | 屈服下的伸张强度 | 23° | ASTM D-638 | 1320 | kgf/cm2 |
| 挤剪强度 | 23° | ASTM D-732 | 710 | kgf/cm2 | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 750 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 900 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 95 | ||
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 140 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 83000 | kgf/cm2 | |
| 弯曲弹性率 | -30° | ASTM D-790 | 90000 | kgf/cm2 | |
| 挤剪强度 | 23° | ASTM D-732 | 530 | kgf/cm2 | |
| 断裂下的延伸率 | ASTM D-638 | 5 | % | ||
| 屈服下的伸张强度 | -30° | ASTM D-638 | 1850 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 13 | mg | ||
| 弯曲弹性率 | 23° | ASTM D-790 | 61000 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 10 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 断裂下的延伸率 | 23° | ASTM D-638 | 5 | % | |
| 弯曲强度 | 23° | ASTM D-790 | 1850 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 8.0 | kgf.cm/cm | |
| 弯曲弹性率 | 80° | ASTM D-790 | 23000 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 100 | ||
| 弯曲弹性率 | 23° | ASTM D-790 | 31000 | kgf/cm2 | |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 250 | kgf/cm2 | |
| 屈服下的伸张强度 | 80° | ASTM D-638 | 650 | kgf/cm2 | |
| 弯曲弹性率 | 80° | ASTM D-790 | 37500 | kgf/cm2 | |
| 电气性能 | 介电损耗 | 60HZ | ASTM D-150 | 0.11 | |
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 介电常数 | 106HZ | ASTM D-150 | 3.6 | ||
| 体积电阻率 | ASTM D-257 | 1012 | Ω.cm | ||
| 介电常数 | 60HZ | ASTM D-150 | 4.0 | ||
| IEC电路 | UL746 | 550 | V | ||
| 介电常数 | 106HZ | ASTM D-150 | 4.6 | ||
| 抗电弧强度 | ASTM D-495 | 121 | S | ||
| 介电常数 | 103HZ | ASTM D-150 | 3.9 | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.10 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.01 | ||
| 介电常数 | 60HZ | ASTM D-150 | 9.0 | ||
| 介电常数 | 103HZ | ASTM D-150 | 8.0 | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介电损耗 | 103HZ | ASTM D-150 | 0.09 | ||
| 体积电阻率 | ASTM D-257 | 1015 | Ω.cm | ||
| 热性能 | 热变形温度 | 4.6kgf/cm2 | ASTM D-648 | 215 | °C |
| 熔点 | DSC | 215-225 | °C | ||
| 燃烧率 | UL94 | HB | |||
| 线性热膨胀系数 | ASTM D-696 | 3.5 | X的10-5cm/cm/°C | ||
| 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 200 | °C | |