ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 耐热,高流动,高刚性 其它 注塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 刚性高，抗撞击性高，可加工性良好，流动性高，耐低温撞击，耐热性高，适于粉刷 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.14 | g/cm³ | |
| 熔流率 | 250℃/3.8kg | ASTM D1238 | 10 | g/10 min | |
| 260℃/5.0kg | ASTM D1238 | 24 | g/10 min | ||
| 收缩率-流动 | 3.00mm | ASTM D955 | 0.40-0.80 | % | |
| 吸水率 | 24hr | ASTM D570 | 0.10 | % | |
| 机械性能 | 洛氏硬度 | R计秤 | ASTM D785 | 116 | |
| 抗张强度 | 3.20mm | ASTM D638 | 56.0 | MPa | |
| 伸长率 | 断裂,3.20mm | ASTM D638 | 150 | % | |
| 弯曲模量 | 3.20mm | ASTM D790 | 2450 | MPa | |
| 弯曲强度 | 3.20mm | ASTM D790 | 92.0 | MPa | |
| 悬壁梁缺口冲击强度 | 3.50mm | ASTM D256 | 680 | J/m | |
| 落锤冲击 | 3.50mm | ASTM D3029 | 65.0 | J | |
| 热性能 | 热变形温度 | 1.8MPa,未退火,3.20mm | ASTM D648 | 112 | ℃ |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 117 | ℃ | ||
| 1.8MPa,未退火,12.7mm | ASTM D648 | 122 | ℃ | ||
| 维卡软化温度 | ASTM D1525 | 143 | ℃ | ||
| 线形膨胀系数-流动 | ASTM D696 | 0.000070 | cm/cm/℃ | ||
| UL阻燃等级 | 1.60mm | UL 94 | HB | ||
| 灼热丝易燃指数 | 1.60mm | AS/NZS 60695.2.12 | 650 | ℃ | |