ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | 衬里，袋子，工业领域：包装，薄膜 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 密度 | ASTM D1505 | 0.950 | g/cm³ | |
| 熔流率 | 190℃/2.16 kg |
ASTM D1238 | 0.050 | g/10 min | |
| 190℃/21.6 kg | ASTM D1238 | 15 | g/10 min | ||
| 抗环境应力开裂 | F50 | ASTM D1693 | > 500 | hr | |
| 机械性能 | 弯曲模量 | ASTM D790 | 1100 |
MPa | |
| 薄膜厚度 - 经测试 | 20 | µm | |||
| 弹性模量 - MD | 20 µm, 吹塑薄膜 | ASTM D882 | 850 | MPa | |
| 弹性模量 - TD |
20 µm, 吹塑薄膜 | ASTM D882 | 1050 | MPa | |
| 抗张强度 | MD: 断裂, 20 µm, 吹塑薄膜 | ASTM D882 | 100 | MPa | |
| TD: 断裂, 20 µm, 吹塑薄膜 | ASTM D882 | 55.0 | MPa | ||
| 伸长率 | MD: 断裂, 20 µm, 吹塑薄膜 | ASTM D882 | 500 | % | |
| TD: 断裂, 20 µm, 吹塑薄膜 | ASTM D882 | 700 | % | ||
| 落锤冲击 | 20 µm, 吹塑薄膜 | ASTM D1709 | 130 | g | |
| Elmendorf Tear Strength | MD: 20.0 µm, Blown Film | ASTM D1922 | 6.9 | kN/m | |
| TD: 20.0 µm, Blown Film | ASTM D1922 | 147.1 | kN/m | ||
| Impact Strength |
20.0 µm, Blown Film | ASTM D3420 | 34.3 | J/cm | |
| 热性能 | 脆化温度 | ASTM D746 | < -70.0 | ℃ | |
| 维卡软化温度 | ASTM D1525 | 127 | ℃ | ||
| 熔体温度 | 180-220 | ℃ | |||