ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重 | ASTM D792 | 1.14 |
g/cm³
|
|
| 熔流率 | 200°C/5.0 kg | ASTM D1238 | 3.4 |
g/10 min
|
|
|
235°C/1.0 kg
|
ASTM D1238 | 36 |
g/10 min
|
||
| 收缩率 |
流动: 3.18 mm
|
ASTM D955 |
0.70 到 0.80
|
% | |
|
横向流动: 3.18 mm
|
ASTM D955 |
0.70 到 0.80
|
% | ||
| 硬度计硬度 | 支撐 A | ASTM D2240 |
87 到 97
|
||
| 机械性能 |
抗泰伯磨耗 | 1000 Cycles, 1000 g, H-22 转轮 | ASTM D3389 | 10.0 |
mg
|
| 拉伸应力 |
50%应变
|
ASTM D412 | 7.58 |
MPa
|
|
|
100%应变
|
ASTM D412 | 11.2 |
MPa
|
||
|
300%应变
|
ASTM D412 | 24.8 |
MPa
|
||
| 抗张强度 | 屈服 | ASTM D412 | 44.8 |
MPa
|
|
| 伸长率 | 断裂 | ASTM D412 | 450 | % | |
| 撕裂强度 | ASTM D624 | 133 |
kN/m
|
||
| 压缩永久变形 | 23°C | ASTM D395 | 25 | % | |