ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 矿物增强 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 矿物填料23%。 性能特点：卤化。 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.56 | g/cm3 | |
| 熔流率 | ASTM D1238 | 20 | g/10min | ||
| 流动收缩率 | 1.00mm | ASTM D955 | 0.10-0.20 | % | |
| 3.00mm | ASTM D955 | 0.30-0.60 | % | ||
| 吸水率 | 24 hr | ASTM D570 | 0.50 | % | |
| 平衡，65%RH | ASTM D570 | 1.8 | % | ||
| 洛氏硬度 | R 计秤 | ASTM D785 | 118 | ||
| 机械性能 | 屈服抗张强度 | -40℃ | ASTM D638 | 61.0 | MPa |
| 23℃ | ASTM D638 | 38.0 | MPa | ||
| 80℃ | ASTM D638 | 24.0 | MPa | ||
| 断裂伸长率 | 23℃ | ASTM D638 | 4.5 | % | |
| 弯曲模量 | -40℃ | ASTM D790 | 6400 | MPa | |
| 23℃ | ASTM D790 | 4400 | MPa | ||
| 80℃ | ASTM D790 | 1200 | MPa | ||
| 屈服弯曲强度 | -40℃ | ASTM D790 | 104 | MPa | |
| 23℃ | ASTM D790 | 63.0 | MPa | ||
| 80℃ | ASTM D790 | 38.0 | MPa | ||
| 压缩强度 | 23℃ | ASTM D695 | 45.0 | MPa | |
| 抗泰伯磨耗 | 1000Cycles,CS-17转轮 | ASTM D1044 | 32.0 | mg | |
| 悬壁梁缺口冲击强度 | -40℃ | ASTM D256 | 45 | J/m | |
| 23℃ | ASTM D256 | 70 | J/m | ||
| 热性能 | 热变形温度 | 0.45MPa,未退火 | ASTM D648 | 205 | ℃ |
| 1.8MPa,未退火 | ASTM D648 | 160 | ℃ | ||
| 流动线形膨胀系数 | ASTM D696 | 0.000042 | ℃ | ||
| UL阻燃等级 | 0.730mm | UL 94 | V-0 | ||
| 电气性能 | 体积电阻率 | ASTM D257 | 1.0E+12 | ohm.cm | |
| 介电强度 | 2.00mm | ASTM D149 | 20 | kV/mm | |
| 耐电弧性 | ASTM D495 | 15.0 | sec | ||
| 漏电起痕指数 | IEC 60112 | 350 | V | ||