ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | 清晰/透明 |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重 | ASTM D792 | 0.992 |
g/cm³
|
|
| 熔流率 | 235°C/1.0 kg | ASTM D1238 | 5.0 |
g/10 min
|
|
| 收缩率 |
流动: 3.18 mm
|
ASTM D955 | 0.80 | % | |
|
横向流动: 3.18 mm
|
ASTM D955 | 0.60 | % | ||
| 硬度计硬度 | 支撐 A | ASTM D2240 | 48 | ||
|
支撐 A, 10 秒
|
ASTM D2240 |
45 到 55
|
|||
| 机械性能 |
抗泰伯磨耗 | 1000 Cycles, 1000 g, H-22 转轮 | ASTM D3389 | 58.9 |
mg
|
| 剥离强度 | 90° | ASTM D429 | 3.6 |
kN/m
|
|
| 拉伸永久变形 | 100% 应变 | ASTM D412 | 4 | % | |
| 拉伸应力 |
50%应变
|
ASTM D412 | 1.50 |
MPa
|
|
|
100%应变
|
ASTM D412 | 1.99 |
MPa
|
||
|
300%应变
|
ASTM D412 | 3.36 |
MPa
|
||
| 抗张强度 | 屈服 | ASTM D412 | 11.3 |
MPa
|
|
| 伸长率 | 断裂 | ASTM D412 | 870 | % | |
| 压缩永久变形 |
23°C, 22.0 hr
|
ASTM D395B | 22 | % | |
|
70°C, 22.0 hr
|
ASTM D395B | 73 | % | ||
|
100°C, 22.0 hr
|
ASTM D395B | 89 | % | ||
| 落锤冲击 | -30°C | ASTM D5420 | 27.0 |
J
|
|