ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
比重 | ASTM D792 | 0.902 |
g/cm³
|
|
| 熔流率 | 200°C/5.0 kg | ASTM D1238 | 0.50 |
g/10 min
|
|
| 收缩率 |
流动: 3.18 mm
|
ASTM D955 | 4.1 | % | |
|
横向流动: 3.18 mm
|
ASTM D955 | 3.8 | % | ||
| 硬度计硬度 | 支撐 A, 10 秒 | ASTM D2240 |
68 到 78
|
||
| 机械性能 |
弯曲模量 | ASTM D790 | 40.7 |
MPa
|
|
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, H-22 转轮 | ASTM D3389 | 263 |
mg
|
|
| 拉伸应力 |
50%应变
|
ASTM D412 | 37.0 |
MPa
|
|
|
100%应变
|
ASTM D412 | 3.52 |
MPa
|
||
|
300%应变
|
ASTM D412 | 4.05 |
MPa
|
||
| 抗张强度 | 屈服 | ASTM D412 | 37.1 |
MPa
|
|
| 伸长率 | 断裂 | ASTM D412 | 300 | % | |
| 撕裂强度 | ASTM D624 | 25.2 |
kN/m
|
||
| 压缩永久变形 | 23°C, 22.0 hr | ASTM D395 | 21 | % | |
| 落锤冲击 | -30°C | ASTM D5420 |
> 36.2
|
J
|
|