ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 |
密度 | ASTM D1505 | 1.925 |
g/cm³
|
|
| 熔流率 | ASTM D1238 | 1.0 |
g/10 min
|
||
| 醋酸乙烯含量 | 4.6 |
wt%
|
|||
薄膜 |
割线模量 |
1% 正割, MD
|
ASTM D882 | 145 |
MPa
|
|
1% 正割, TD
|
ASTM D882 | 169 |
MPa
|
||
| 抗张强度 |
MD: 断裂
|
ASTM D882 | 25.9 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 24.7 |
MPa
|
||
|
伸长率
|
MD: 断裂
|
ASTM D882 | 180 | % | |
|
TD: 断裂
|
ASTM D882 | 580 | % | ||
| 落锤冲击 | ASTM D1709 | 190 |
g
|
||
| 伸长率 |
MD
|
ASTM D1922 | 200 |
g
|
|
|
TD
|
ASTM D1922 | 90 |
g
|
||
| 热性能 | 维卡软化温度 | ASTM D1525 | 88.9 |
°C
|
|
| 光学性能 | 光泽度 | ASTM D2457 | 71 | ||
| 雾度 | ASTM D1003 | 6.4 | % | ||