ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 透明,耐热 其它 注塑 | 外观颜色 | |
| 该料用途 | 电器,光盘的外壳,商用设备,电子零件,照明装置,交通,家用器具,休闲,包装材料 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792,ISO 1183/A | 1.20 | g/cm3 | |
| 熔流率 | 300℃/1.2kg | ASTM D1238,ISO 1133 | 9.0 | g/10min | |
| 流动收缩率 | ASTM D955 | 0.50-0.70 | % | ||
| 流量收缩率 | ISO 294-4 | 0.50-0.70 | % | ||
| 吸水率 | 23℃,24hr | ASTM D570，ISO 62 | 0.15 | % | |
| 平衡，23℃，50%RH | ASTM D570，ISO 62 | 0.32 | % | ||
| 洛氏硬度 | M计秤 | ASTM D785 | 73 | ||
| R计秤 | ASTM D785 | 118 | |||
| 机械性能 | 拉伸模量 | ASTM D638 | 2410 | MPa | |
| ISO 527-2/50 | 2300 | MPa | |||
| 屈服抗张强度 | ASTM D638 | 60.0 | MPa | ||
| 屈服抗张强度 | ISO 527-2/50 | 60.0 | MPa | ||
| 断裂抗张强度 | ASTM D638 | 71.0 | MPa | ||
| 断裂抗张强度 | ISO 527-2/50 | 71.0 | MPa | ||
| 屈服伸长率 | ASTM D638 | 6.0 | % | ||
| 屈服伸长率 | ISO 527-2/50 | 6.0 | % | ||
| 断裂伸长率 | ASTM D638 | 150 | % | ||
| 断裂伸长率 | ISO 527-2/50 | 150 | % | ||
| 弯曲模量 | ASTM D790 | 2410 | MPa | ||
| 弯曲模量 | ISO 178 | 2400 | MPa | ||
| 弯曲强度 | ASTM D790 | 96.5 | MPa | ||
| 弯曲强度 | ISO 178 | 97.0 | MPa | ||
| 耐磨耗性 | ASTM D1044 | 45 | % | ||
| 简支梁缺口冲击强度 | 23℃ | ISO 179/1eA | 35 | kJ/cm2 | |
| 悬壁梁缺口冲击强度 | 23℃ | ASTM D256 | 910 | J/m |
|
| 23℃ | ISO 180/A | 90 | kJ/cm2 | ||
| 无缺口悬壁梁冲击 | 23℃ | ASTM D256,ISO 180 | 无断裂 | ||
| 装有测量仪表的落镖冲击 | 23℃,总能量 | ASTM D3763 | 87.0 | J | |
| 热性能 | 热变形温度 | 0.45MPa,退火 | ASTM D648,ISO 75-2/B | 144 | ℃ |
| 1.8MPa,未退火 | ASTM D648 | 128 | ℃ | ||
| 1.8MPa,未退火 | ISO 75-2/A | 125 | ℃ | ||
| 1.8MPa,退火 | ASTM D648,ISO 75-2/A | 141 | ℃ | ||
| 维卡软化温度 | ISO 306/B50, ASTM D1525 | 149 | ℃ | ||
| 球压温度 | IEC 60335-1 | 125 | ℃ | ||
| 流动线形膨胀系数 | -40到82℃ | ASTM D696 | 0.000068 | cm/cm/℃ | |
| UL 阻燃等级 | 1.60 mm | UL 94 | HB | ||
| 3.20 mm | UL 94 | HB | |||
| 极限氧指数 | ISO 4589-2 | 26 | % | ||
| 平均燃烧程度 | ASTM D635 | 3 | cm | ||
| 电气性能 | 体积电阻率 | ASTM D257 | 2.0E+17 | ohm.cm | |
| 介电强度 | ASTM D149,IEC 60243-1 | 17 | kV/mm | ||
| 介电常数 | 60Hz | ASTM D150 | 3.00 | ||
| 1 MHz | ASTM D150 | 3.00 | |||
| 耗散因数 | 50Hz | ASTM D150 | 0.0010 | ||
| 1 MHz | ASTM D150 | 0.0020 | |||
| 漏电起痕指数 | 2.00mm,解决方案A | IEC 60112 | 250 | V | |
| 光学性能 | 折射率 | ASTM D542,ISO 489 | 1.586 | ||
| 透射率 | ASTM D1003 | 89.0 | % | ||
| 雾度 | ASTM D1003 | 1.0 | % | ||