ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 阻燃性 | UL 94 | V-0 | |||
| 比重 | ASTM D-792 | 1.69 | ||||
| 机械性能 | 弯曲强度 | ASTM D-790 | 186(1900) | MPa(Kg/cm2) | ||
| 拉伸强度 | ASTM D-638 | 127(1300) | MPa(Kg/cm2) | |||
| 成型收缩率 | 机械方向 | ASTM D-955 | 0.3 | % | ||
| 横向 | ASTM D-955 | 0.9 | % | |||
| 冲击强度 | 缺口 | ASTM D-256 | 69(7) | J/M(kg.cm/cm) | ||
| 无缺口 | ASTM D-256 | 216(22) | J/M(kg.cm/cm) | |||
| 伸长率 | ASTM D-638 | 1.2 | % | |||
| 洛氏硬度 | ASTM D-785 | 120 | Rscal | |||
| 拉伸模量 | ASTM D-790 | 11(1.1) | GPa(×105kg/cm2) | |||
| 电气性能 | 介电常数 | 1MHz | ASTM D-150 | 3.3 | ||
| 介电强度 | ASTM D-149 | 16 | KV/mm | |||
| 损耗因素 | 1MHz | ASTM D-150 | 0.0015 | |||
| 体积电阻率 | ASTM D-257 | 1×1016 | Ω.cm | |||
| 热性能 | 热变形温度 | 18.6kg/cm2 | ASTM D-648 | ＞250 | ℃ | |
| 热膨胀系数 | 0.29(0.25) | W/M.K(kcal/m.hr.℃) | ||||
| 线性热膨胀系数 | Tosoh Method | 2.9 | ×10-51/K(×10-5cm/cm℃) | |||