ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | 透明 |
| 该料用途 | |||
| 备注说明 | 特性：高抗冲 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 200℃×5N | ASTM D-1238 | 2.0 | g/10min |
| 熔体流动速率 | 220℃×100N | ASTM D-1238 | 28 | g/10min | |
| 物理性能 | 成型收缩率 | 2mm | 0.4-0.6 | % | |
| 全光线透过率 | 2mm | ASTM D-1003 | 90 | % | |
| 比重 | ASTM D-792 | 1.09 | |||
| 雾度 | 2mm | ASTM D-1003 | 2.0 | % | |
| 机械性能 | 弯曲强度 | ASTM D-790 | 62 | MPa | |
| 拉伸强度 | ASTM D-638 | 37 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 110 | R | ||
| IZOD冲击强度 | 1/4〃带缺口 | ASTM D-256 | 185 | J/m | |
| 弯曲弹性模量 | ASTM D-790 | 1950 | MPa | ||
| 洛氏硬度 | ASTM D-785 | 46 | M | ||
| 热性能 | 热变形温度 | 12.7mm,1.82MPa | ASTM D-648 | 84 | ℃ |
| 热变形温度 | 6.4mm,1.82MPa | ASTM D-648 | 80 | ℃ | |
| 燃烧性 | UL 94 | 1.5mmHB | |||
| 维卡软化点 | 50N | ASTM D-1525 | 85 | ℃ | |