ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 其它性能 | 拉伸调整 | 200%伸长率 | ASTM D-412 | 15 | % |
| 机械性能 | 300%模量伸长率 | ASTM D-412（ASTM D-638） | 9.0 | MPa | |
| 极限伸长率 | ASTM D-412（ASTM D-638） | 530 | % | ||
| 模具刚度系数 | -50℃ | ASTM D-1053 | 276.0 | MPa | |
| 模具刚度系数 | 23℃ | ASTM D-1053 | 5.5 | MP | |
| 模具刚度系数 | 0℃ | ASTM D-1053 | 6.3 | MPa | |
| Brookfield Viscosity | 15% T.S.in cyclohexanone | RVT Spindle #2,20 RPM,23℃ | 15 | cps | |
| 比重 | ASTM D-792 | 1.11 | |||
| 压缩调整 | 22 hours @ 70℃ | ASTM D-395 | 77 | % | |
| 断裂强度 | ASTM D-624，Die C | 64.8 | KN/m | ||
| 模具刚度系数 | -55℃ | ASTM D-1053 | 379.0 | MPa | |
| 开口断裂强度 | ASTM D-470 | 21.4 | KN/m | ||
| 100%模量伸长率 | ASTM D-412（ASTM D-638） | 4.8 | MPa | ||
| Brookfield Viscosity | 15% T.S.in THF | RVT Spindle #2,20 RPM,23℃ | 900 | cps | |
| Taber Abrasion | CS-17 wheel,1000g load | ASTM D-1044 | 2.8 | mg/1000 cycles | |
| 洛氏硬度 | ASTM D-2240 | 80A | |||
| 模具刚度系数 | -40℃ | ASTM D-1053 | 55.2 | MPa | |
| 模具刚度系数 | -20℃ | ASTM D-1053 | 9.3 | MPa | |
| 压缩调整 | 22 hours @ 23℃ | ASTM D-395 | 24 | % | |
| 拉伸强度 | ASTM D-412（ASTM D-638） | 31.0 | MPa | ||
| 热性能 | 维卡软化点 | ASTM D-1525 | 71 | ℃ | |
| 玻璃化转变温度 | DSC | -38 | ℃ | ||