| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 机械性能 | 300%模量伸长率 | | ASTM D-412（ASTM D-638） | 13.1 | MPa |
| 压缩调整 | 22 hours @ 70℃ | ASTM D-395 | 83 | % |
| 比重 | | ASTM D-792 | 1.21 | |
| 100%模量伸长率 | | ASTM D-412（ASTM D-638） | 5.2 | MPa |
| 拉伸调整 | | ASTM D-412 | 11 | % |
| Split Tear Resistance | | ASTM D-470 | 25.6 | KN/m |
| Brookfield Viscosity | 15% T.S.in cyclohexanone | RVT Spindle #2,20 RPM,23℃ | 2400 | cps |
| 极限伸长率 | | ASTM D-412（ASTM D-638） | 460 | % |
| 压缩调整 | 22 hours @ 23℃ | ASTM D-395 | 23 | % |
| 洛氏硬度 | | ASTM D-2240 | 85A | |
| 吸水性 | CS-17 wheel,1000g load | ASTM D-1044 | 2.5 | mg/1000 cycles |
| 断裂强度 | | ASTM D-624，Die C | 73.6 | KN/m |
| Adhesion to PET | | TP-141 | 0.11 | KN/m |
| 拉伸强度 | | ASTM D-412（ASTM D-638） | 49.0 | MPa |
| Brookfield Viscosity | 15% T.S.in THF | RVT Spindle #2,20 RPM,23℃ | 475 | cps |
| 热性能 | 维卡软化点 | | ASTM D-1525 | 70 | ℃ |
| 玻璃化转变温度 | | DSC | -28 | ℃ |
| 其它性能 | Gradient Bar Tack Temperature | | | 121 | ℃ |
| Melt Viscosity @ 204 C(400℃) | | ASTM D-1084-88 | 28,000 | cps |
| Open Time | | ASTM D-4497-94 | ＜5 | sec |
| T-peel,Aluminum Foil | | ASTM D-1876-72 | 0.9 | KN/m |
| Ring and Ball Softening Point | | ASTM E-28-92 | 161 | ℃ |
| T-peel,Mylar Film | | ASTM D-1876-72 | 5.0 | KN/m |