ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔流率 | 190°C/2.16 kg | ASTM D1238 | 0.40 |
g/10 min
|
| 醋酸乙烯含量 | ExxonMobil Method | 12.8 |
wt%
|
||
| 机械性能 | 割线模量 | 1% 正割, MD | ASTM D882 | 80.4 |
MPa
|
| 1% 正割, TD | ASTM D882 | 89.9 |
MPa
|
||
| 抗张强度 |
MD: 断裂
|
ASTM D882 | 33.9 |
MPa
|
|
|
TD: 断裂
|
ASTM D882 | 34.6 |
MPa
|
||
| 伸长率 |
MD: 断裂
|
ASTM D882 | 360 |
%
|
|
|
TD: 断裂
|
ASTM D882 | 660 |
%
|
||
| 落锤冲击 | ASTM D1709A | 710 | g | ||
| 埃尔曼多夫抗撕强度 |
MD
|
ASTM D1922 | 66 | g | |
|
TD
|
ASTM D1922 | 82 | g | ||
| 热性能 | 维卡软化温度 | ASTM D1525 | 76.0 |
°C
|
|