ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 电动工具配件 注塑 | 外观颜色 | |
| 该料用途 | 家用货品 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792, ISO 1183 | 1.63 | g/cm³ | |
| 熔流率 | 250°C/5.0 kg | ASTM D1238 | 42 | g/10 min | |
| 溶化体积流率 | MVR250°C/5.0 kg | ISO 1133 | 29.0 | cm³/10min | |
| 收缩率 | 流动 | Internal Method | 0.10 到 0.50 | % | |
| 流动: 3.20 mm | Internal Method | 0.50 到 0.70 | % | ||
| 横向流动 | Internal Method | 0.40 到0.80 | % | ||
| 横向流动: 3.20 mm | Internal Method | 0.50 到 1.0 | % | ||
| 吸水率 | 饱和, 23°C | ISO 62 | 0.090 | % | |
| 平衡, 23°C, 50% RH | ISO 62 | 0.070 | % | ||
| 特定体积 | ASTM D792 | 0.610 | cm³/g | ||
| 洛氏硬度 | (R 计秤) | ASTM D785, ASTM D785 | 119 | ||
| 球压硬度 | (H 358/30) | ISO 2039-1 | 118 | MPa | |
| 机械性能 | 拉伸模量 | ASTM D638 | 12000 | MPa | |
| ISO 527-2/1 | 10000 | MPa | |||
| 抗张强度 | 屈服 | ASTM D638 | 120 | MPa | |
| 屈服 | ISO 527-2/5 | 120 | MPa | ||
| 断裂 | ASTM D638 | 120 | MPa | ||
| 断裂 | ISO 527-2/5 | 120 | MPa | ||
| 伸长率 | 屈服 | ASTM D638 | 2.0 | % | |
| 屈服 | ISO 527-2/5 | 1.9 | % | ||
| 断裂 | ASTM D638 | 2.0 | % | ||
| 断裂 | ISO 527-2/5 | 1.9 | % | ||
| 弯曲模量 | 50.0 mm 跨距 | ASTM D790 | 9800 | MPa | |
| ISO 178 | 9500 | MPa | |||
| ISO 178 | 180 | MPa | |||
| 断裂, 50.0 mm 跨距 | ASTM D790 | 186 | MPa | ||
| 抗泰伯磨耗 | 1000 Cycles,1000 g, CS-17 转轮 | Internal Method | 22.0 | mg | |
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eA | 6.0 | kJ/m² | |
| 23°C | ISO 179/1eA | 7.0 | kJ/m² | ||
| 简支梁缺口冲击强度 | -30°C | ISO 179/1eU | 50 | kJ/m² | |
| 23°C | ISO 179/1eU | 50 | kJ/m² | ||
| 悬壁梁缺口冲击强度 | -30°C | ASTM D256 | 57.0 | J/m | |
| 23°C | ASTM D256 | 60.0 | J/m | ||
| -30°C | ISO 180/1A |
6.00 | kJ/m² | ||
| 23°C | ISO 180/1A | 7.00 | kJ/m² | ||
| 无缺口悬臂梁冲击 | 23°C | ASTM D4812 | 620 | J/m | |
| -30°C | ISO 180/1U | 45.0 | kJ/m² | ||
| 23°C | ISO 180/1U | 45.0 | kJ/m² | ||
| 装有测量仪表的落镖冲击 | 23°C, Total Energy | ASTM D3763 | 5.00 | J | |
| 热性能 | 热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 212 | °C |
| 0.45 MPa, 未退火, 100 mm 跨距 | ISO 75-2/Be | 220 | °C | ||
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 200 | °C | ||
| 1.8 MPa, 未退火, 100 mm 跨距 | ISO 75-2/Ae | 195 | °C | ||
| 1.8 MPa, 未退火, 64.0 mm 跨距 | ISO 75-2/Af | 200 | °C | ||
| 维卡软化温度 | ASTM D1525 | 200 | °C | ||
| ISO 306/B50 | 200 | °C | |||
| ISO 306/B120 | 200 | °C | |||
| ISO 306/A50 | 220 | °C | |||
| Ball PressureTest125°C | IEC 60695-10-2 | Pass | |||
| 线形膨胀系数 | 流动: -40 到 40°C | ASTM E831, ISO 11359-2 | 0.000025 | cm/cm/°C | |
| 流动: 23 到 80°C | ISO 11359-2 | 0.000025 | cm/cm/°C | ||
| 横向: -40 到 40°C | ASTM E831, ISO 11359-2 | 0.000089 | cm/cm/°C | ||
| 横向: 23 到 80°C | ISO 11359-2 | 0.00012 | cm/cm/°C | ||
| 导热系数 | ISO 8302 | 0.25 | |||
| 电气性能 | 体积电阻率 | IEC 60093 | > 1.0E+15 | ohms | |
| ASTM D257, IEC 60093 | > 1.0E+15 | ohm·cm | |||
| 介电强度 | 1.60 mm, in Oil | ASTM D149 | 24 | kV/mm | |
| 3.20 mm, in Air | ASTM D149 | 19 | kV/mm | ||
| 0.800 mm, 在油中 | IEC 60243-1 | 23 | kV/mm | ||
| 1.60 mm, 在油中 | IEC 60243-1 | 22 | kV/mm | ||
| 3.20 mm, 在油中 | IEC 60243-1 | 16 | kV/mm | ||
| 介电常数 | 100 Hz | ASTM D150, IEC 60250 | 3.80 | ||
| 1 MHz | ASTM D150 | 3.70 | |||
| 50 Hz | IEC 60250 | 3.30 | |||
| 60 Hz | IEC 60250 | 3.30 | |||
| 1 MHz | IEC 60250 | 3.30 | |||
| 耗散因数 | 100 Hz | ASTM D150, IEC 60250 | 0.0020 | ||
| 1 MHz | ASTM D150 | 0.020 | |||
| 50 Hz | IEC 60250 | 0.0010 | |||
| 60 Hz | IEC 60250 | 0.0010 | |||
| 1 MHz | IEC 60250 | 0.010 | |||
| 耐电弧性 (PLC) | ASTM D495 | PLC 6 | |||
| 漏电起痕指数 | IEC 60112 | 175 | V | ||
| 解决方案 B | IEC 60112 | 125 | V | ||