ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | 农业用宽幅薄膜，是透明性，加工性和机械物性优秀的产品 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.931 | g/cc | ||
| 熔体流动速率 | ASTM D-1238 | 0.8 | g/10min | |||
| 机械性能 | 拉伸断裂强度 | MD | ASTM D-882 | 270 | kg/cm2 | |
| TD | ASTM D-882 | 250 | kg/cm2 | |||
| 断裂拉伸强度 | ASTM D638 | 195 | kg/cm2 | |||
| 断裂伸长率 | MD | ASTM D-882 | 350 | % | ||
| TD | ASTM D-882 | 650 | % | |||
| 断裂伸长率 | ASTM D-638 | 760 | % | |||
| 拉伸抗热强度 | MD | ASTM D-1004 | 80 | kg/cm | ||
| TD | ASTM D-1004 | 85 | kg/cm | |||
| 热性能 | 维卡软化点 | ASTM D-1525 | 77 | ℃ | ||
| 熔点 | ASTM D-2117 | 98 | ℃ | |||
| 其它性能 | 厚度 | HCC Method | 0.06 | ㎜ | ||
| 混浊度 | ASTM D-1009 | 3.0 | % | |||
| 醋酸乙烯含量 | HCC Method | 9.5 | Wt% | |||
| 下降冲击强度 | ASTM D-1709 | ＞400 | g | |||