ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 薄膜 其它 | 外观颜色 | |
| 该料用途 | 收缩、重包装、暖棚用薄膜 | ||
| 备注说明 | 特性：机械物性热收缩性、加工性 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.920 | g/cc | ||
| 熔体流动速率 | ASTM D-1238 | 3.0 | g/10min | |||
| 机械性能 | 断裂拉伸强度 | ASTM D-638 | 165 | kg/cm2 | ||
| 拉伸抗热强度 | MD | ASTM D-1004 | 110 | kg/cm | ||
| TD | ASTM D-1004 | 105 | kg/cm | |||
| 下降冲击强度 | ASTM D-1709 | 200 | g | |||
| 断裂拉伸强度 | MD | ASTM D-882 | 280 | kg/cm2 | ||
| TD | ASTM D-882 | 250 | kg/cm2 | |||
| 断裂伸长率 | ASTM D-638 | 750 | % | |||
| 断裂伸长率 | MD | ASTM D-882 | 250 | % | ||
| TD | ASTM D-882 | 600 | % | |||
| 热性能 | 熔点 | ASTM D-2117 | 110 | ℃ | ||
| 维卡软化点 | ASTM D-1525 | 94 | ℃ | |||
| 其它性能 | 混浊度 | ASTM D1009 | 15.0 | % | ||
| 厚度 | HCC | 0.06 | ㎜ | |||