| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 物理性能 | 收缩率 | - | 平行流动方向 | ASTM D955 | 0.011 | cm/cm |
| - | 垂直流动方向 | ASTM D955 | 0.017 | cm/cm |
| 机械性能 | 弯曲模量 | 23 ℃, 0.00 mm, Injection Molded, Procedure A, Method I (3 point load), 0.00 mm, Type I, Secant | ASTM D790 | 1680 | MPa |
| 弯曲强度 | 23 ℃, 0.00 mm, Injection Molded, Method I (3 point load), Procedure A, 0.00 mm, Type I | ASTM D790 | 53 | MPa |
| 断裂点伸长率 | 23℃, 0.00 mm, Compression Molded, Type I | ASTM D638 | 150 | % |
| 缺口冲击强度 | 23℃, 0.00 mm, 0.0 mm, Injection Molded, Method A, Across Flow | ASTM D256 | No Break | J/m |
| 非缺口冲击强度 | - | -40 ℃, 0.00 mm | ASTM D256 | No Break | J/m |
| - | 23 ℃, 0.00 mm | ASTM D256 | No Break | J/m |
| 热性能 | 熔点 | | DSC | 225 | ℃ |