ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||||
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 5 | g/10min | |||
| 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 5 | g/10min | ||||
| 单体含量 | Internal Method | 9.7 | % | |||||
| 物理性能 | 比重 | ASTM D-792 | 0.93 | g/cm3 | ||||
| 比重 | ISO 1183 | 0.93 | g/cm3 | |||||
| 机械性能 | 拉伸屈服强度 | Compression Molded | ASTM D-638 | 7.67 | MPa | |||
| 拉伸屈服强度 | Compression Molded | ISO 527-2/508 | 7.67 | MPa | ||||
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 19.5 | MPa | ||||
| 拉伸断裂强度 | Compression Molded | ISO 527-2/508 | 19.5 | MPa | ||||
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 580 | % | ||||
| 拉伸断裂伸长率 | Compression Molded | ISO 527-2/508 | 580 | % | ||||
| 薄膜厚度-Tested | 50.8 | um | ||||||
| 拉伸屈服强度 | 50.8um | ASTM D-882 |
| MPa | ||||
| 拉伸屈服强度 | 50.8um | ISO 527-3 |
| MPa | ||||
| 拉伸断裂强度 | 50.8um | ASTM D-882 |
| MPa | ||||
| 拉伸断裂强度 | 50.8um | ISO 527-3 |
| MPa | ||||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 |
| % | ||||
| 拉伸断裂伸长率 | 50.8um | ISO 527-3 |
| % | ||||
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 |
| g | ||||
| 埃尔曼多夫撕裂强度 | 50.8um | ISO 6383-2 |
| N | ||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 76.1 | ℃ | ||||
| 维卡软化点 | ISO 306 | 76.1 | ℃ | |||||
| 熔融温度 | Internal Method | 96.1 | ℃ | |||||
| 光学性能 | 光泽度 | 45°，50.8um | ASTM D-2457 | 74 | ||||
| 雾度 | 50.8um | ISO 14782 | 4 | % | ||||
| 雾度 | 50.8um | ASTM D-1003 | 4 | % | ||||
| 熔体温度 | 196 | ℃ | ||||||