ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 涂覆 其它 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.918 | g/cm3 | ||
| 熔体流动速率 | 190℃/2.160kg | ASTM D-1238 | 7.5 | g/10min | ||
| 物理性能 | 混浊度 | ASTM D-1003 | 10.6 | % | ||
| 光泽度 | 60℃ | ASTM D-2457 | 8.2 | % | ||
| 机械性能 | 断裂伸长率 | ASTM D-638 | 611 | % | ||
| 极限强度 | MD | ASTM D-882 | 22 | MPa | ||
| TD | ASTM D-882 | 17 | MPa | |||
| 击穿强度 | Baskem Method | 37 | J/mm | |||
| 断裂伸长率 | MD | ASTM D-882 | 330 | % | ||
| TD | ASTM D-882 | 1100 | % | |||
| 摩擦系数 | ASTM D-1894 | 0.86 | ||||
| Elmendorf撕裂强度 | MD | ASTM D-1922 | NDd | kgF/cm | ||
| TD | ASTM D-1922 | 33 | kgF/cm | |||
| 断裂拉伸强度 | ASTM D-638 | 10 | MPa | |||
| 热性能 | 初始密封温度 | Braskem Method | 100 | ℃ | ||
| 维卡软化温度 | ASTM D-1525 | 87 | ℃ | |||
| 其它性能 | 最小推荐厚度 | 10 | μm | |||
| Dard impact resistance | ASTM D-1709 | 75 | gF/50%f | |||