| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
0.978to1.02 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStrength(0.762mm) |
|
ASTMD412 |
19.0 |
MPa |
| ELASTOMERS |
伸长率(断裂,0.762mm) |
|
ASTMD412 |
600 |
% |
| ELASTOMERS |
TearStrength2(0.762mm) |
|
ASTMD624 |
70.1 |
kN/m |
| 硬度 |
肖氏硬度 |
邵氏A |
ASTMD2240 |
82to88 |
|
| 硬度 |
肖氏硬度 |
邵氏A,15秒 |
ASTMD2240 |
78to84 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-60.0 |
°C |
| 热性能 |
Deformation3 |
121°C,889.0µm |
ASTMD2219 |
5.5 |
% |
| 热性能 |
Deformation3 |
150°C,889.0µm |
ASTMD2219 |
8.9 |
% |
| 老化 |
ChangeinTensileStrengthinAir4(136°C,168hr) |
|
ULUnspecified |
0.0 |
% |
| 老化 |
ChangeinUltimateElongationinAir4(136°C,168hr) |
|
ULUnspecified |
-5.0 |
% |
| 老化 |
ChangeinTensileStrength4(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
-10 |
% |
| 老化 |
ChangeinUltimateElongation4(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
0.0 |
% |
| 电气性能 |
体积电阻率(23°C) |
|
ASTMD257 |
9.8E+15 |
ohms·cm |
| 电气性能 |
介电强度(23°C) |
|
ASTMD149 |
28 |
kV/mm |
| 电气性能 |
介电常数(23°C,1MHz) |
|
ASTMD150 |
2.30 |
|
| 电气性能 |
耗散因数(23°C,1MHz) |
|
ASTMD150 |
1.0E-4 |
|