| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.22to1.26 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
抗张强度2 |
|
ASTMD412 |
24.8 |
MPa |
| ELASTOMERS |
伸长率2(断裂) |
|
ASTMD412 |
500 |
% |
| 硬度 |
肖氏硬度 |
邵氏A |
ASTMD2240 |
93to99 |
|
| 硬度 |
肖氏硬度 |
邵氏A,15秒 |
ASTMD2240 |
89to95 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-60.0 |
°C |
| 老化 |
ChangeinTensileStrengthinAir3(136°C,168hr) |
|
ULUnspecified |
0.0 |
% |
| 老化 |
ChangeinUltimateElongationinAir3(136°C,168hr) |
|
ULUnspecified |
-2.0 |
% |
| 老化 |
ChangeinTensileStrength3(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
-8.0 |
% |
| 老化 |
ChangeinUltimateElongation3(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
-4.0 |
% |
| 电气性能 |
体积电阻率(23°C) |
|
ASTMD257 |
4.0E+15 |
ohms·cm |
| 电气性能 |
DielectricConstant(23°C,100MHz) |
|
ASTMD150 |
2.30 |
|
| 电气性能 |
DissipationFactor(23°C,100MHz) |
|
ASTMD150 |
5.0E-4 |
|
| 可燃性 |
极限氧指数(3.18mm) |
|
ASTMD2863 |
25 |
% |