| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.23to1.27 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStrength(1.02mm) |
|
ASTMD412 |
15.9 |
MPa |
| ELASTOMERS |
TensileElongation(Break,1.02mm) |
|
ASTMD412 |
330 |
% |
| 硬度 |
肖氏硬度 |
邵氏A |
ASTMD2240 |
82to88 |
|
| 硬度 |
肖氏硬度 |
邵氏A,15秒 |
ASTMD2240 |
73to79 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-37.0 |
°C |
| 热性能 |
Deformation-retention,1hour(150°C,1.27mm) |
|
|
61 |
% |
| 老化 |
ChangeinTensileStrengthinAir2(136°C,168hr) |
|
ULUnspecified |
17 |
% |
| 老化 |
空气中极限伸长率的变化率2(136°C,168hr) |
|
ULUnspecified |
-7.0 |
% |
| 老化 |
ChangeinTensileStrength2(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
24 |
% |
| 老化 |
ChangeinUltimateElongation2(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
-5.0 |
% |
| 电气性能 |
体积电阻率(23°C) |
|
ASTMD257 |
1.0E+14 |
ohms·cm |
| 可燃性 |
极限氧指数(3.18mm) |
|
ASTMD2863 |
22 |
% |