| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.11 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
1.0 |
g/10min |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress2,3(100%Strain,0.508mm) |
|
ASTMD412 |
5.00 |
MPa |
| ELASTOMERS |
TensileStress2,3(300%Strain,0.508mm) |
|
ASTMD412 |
6.34 |
MPa |
| ELASTOMERS |
TensileStrength2,3(Break,0.508mm) |
|
ASTMD412 |
12.1 |
MPa |
| ELASTOMERS |
TensileElongation2,3(Break,0.508mm) |
|
ASTMD412 |
700 |
% |
| 硬度 |
肖氏硬度(邵氏A) |
|
ASTMD2240 |
87 |
|
| 热性能 |
连续使用温度 |
|
ASTMD794 |
105 |
°C |
| 热性能 |
RTIElec |
|
UL746 |
50.0 |
°C |
| 热性能 |
RTIStr |
|
UL746 |
50.0 |
°C |
| 老化 |
空气中拉伸强度的变化率(136°C,168hr) |
|
ASTMD573 |
5.0 |
% |
| 老化 |
空气中极限伸长率的变化率(136°C,168hr) |
|
ASTMD573 |
-9.0 |
% |
| 老化 |
ChangeinTensileStrength(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-72 |
% |
| 老化 |
ChangeinUltimateElongation(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-55 |
% |
| 电气性能 |
体积电阻率 |
23°C |
ASTMD257 |
3.1E+15 |
ohms·cm |
| 电气性能 |
体积电阻率 |
50°C |
ASTMD257 |
6.6E+13 |
ohms·cm |
| 电气性能 |
介电强度 |
|
ASTMD149 |
44 |
kV/mm |
| 电气性能 |
介电常数(1kHz) |
|
ASTMD150 |
2.50 |
|
| 可燃性 |
UL阻燃等级(1.5mm,AllColors) |
|
UL94 |
HB |
|
| 可燃性 |
极限氧指数 |
|
ASTMD2863 |
18 |
% |