| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.00 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(200°C/5.0kg) |
|
ASTMD1238 |
19 |
g/10min |
| 机械性能 |
弯曲模量 |
|
ASTMD790 |
103 |
MPa |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress2,3(100%Strain,0.508mm) |
|
ASTMD412 |
4.52 |
MPa |
| ELASTOMERS |
TensileStress2,3(300%Strain,0.508mm) |
|
ASTMD412 |
6.21 |
MPa |
| ELASTOMERS |
TensileStrength2,3(Yield,0.508mm) |
|
ASTMD412 |
16.9 |
MPa |
| ELASTOMERS |
TensileElongation2,3(Break,0.508mm) |
|
ASTMD412 |
650 |
% |
| 硬度 |
肖氏硬度(邵氏A) |
|
ASTMD2240 |
84 |
|
| 热性能 |
连续使用温度 |
|
UL1581 |
105 |
°C |
| 热性能 |
脆化温度 |
|
ASTMD746 |
<-60.0 |
°C |
| 热性能 |
RTIElec |
|
UL746 |
90.0 |
°C |
| 热性能 |
RTIStr |
|
UL746 |
90.0 |
°C |
| 老化 |
空气中拉伸强度的变化率(136°C,168hr) |
|
ASTMD573 |
4.0 |
% |
| 老化 |
空气中极限伸长率的变化率(136°C,168hr) |
|
ASTMD573 |
-8.0 |
% |
| 老化 |
ChangeinTensileStrength(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-5.0 |
% |
| 老化 |
ChangeinUltimateElongation(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-7.0 |
% |
| 电气性能 |
体积电阻率(50°C) |
|
ASTMD257 |
9.6E+16 |
ohms·cm |
| 电气性能 |
介电强度 |
|
ASTMD149 |
38 |
kV/mm |
| 电气性能 |
介电常数 |
1kHz |
ASTMD150 |
2.36 |
|
| 电气性能 |
介电常数 |
1MHz |
ASTMD150 |
2.37 |
|
| 电气性能 |
耗散因数 |
1kHz |
ASTMD150 |
1.0E-4 |
|
| 电气性能 |
耗散因数 |
1MHz |
ASTMD150 |
1.2E-3 |
|
| 可燃性 |
UL阻燃等级(0.8mm,AllColors) |
|
UL94 |
HB |
|
| 可燃性 |
极限氧指数 |
|
ASTMD2863 |
18 |
% |