| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.30 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率） |
|
ASTMD1238 |
0.10 |
g/10min |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress2,3(100%Strain,0.508mm) |
|
ASTMD412 |
3.03 |
MPa |
| ELASTOMERS |
TensileStress2,3(300%Strain,0.508mm) |
|
ASTMD412 |
4.48 |
MPa |
| ELASTOMERS |
TensileStrength2,3(Break,0.508mm) |
|
ASTMD412 |
11.0 |
MPa |
| ELASTOMERS |
TensileElongation2,3(Break,0.508mm) |
|
ASTMD412 |
600 |
% |
| 硬度 |
肖氏硬度(邵氏A) |
|
ASTMD2240 |
72 |
|
| 热性能 |
连续使用温度 |
|
ASTMD794 |
105 |
°C |
| 热性能 |
脆化温度 |
|
ASTMD746 |
-47.0 |
°C |
| 热性能 |
RTIElec |
|
UL746 |
50.0 |
°C |
| 热性能 |
RTIStr |
|
UL746 |
50.0 |
°C |
| 老化 |
ChangeinTensileStrengthinAir(158°C,168hr) |
|
ASTMD573 |
7.0 |
% |
| 老化 |
ChangeinUltimateElongationinAir(158°C,168hr) |
|
ASTMD573 |
-11 |
% |
| 老化 |
ChangeinTensileStrength(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-16 |
% |
| 老化 |
ChangeinUltimateElongation(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-13 |
% |
| 电气性能 |
介电常数(1kHz) |
|
ASTMD150 |
2.60 |
|
| 可燃性 |
UL阻燃等级 |
1.5mm,BK |
UL94 |
V-1 |
|
| 可燃性 |
UL阻燃等级 |
1.5mm,NT,WT,YL |
UL94 |
V-0 |
|
| 可燃性 |
极限氧指数 |
|
ASTMD2863 |
29 |
% |