| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.30 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(230°C/2.16kg) |
|
ASTMD1238 |
0.30 |
g/10min |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
抗张强度(断裂) |
|
ASTMD412 |
12.4 |
MPa |
| ELASTOMERS |
伸长率(断裂) |
|
ASTMD412 |
600 |
% |
| ELASTOMERS |
撕裂强度2 |
横向流量:23°C |
ASTMD624 |
39.4 |
kN/m |
| ELASTOMERS |
撕裂强度2 |
流量:23°C |
ASTMD624 |
44.0 |
kN/m |
| ELASTOMERS |
CompressionSet(125°C,70hr) |
|
ASTMD395 |
14 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,1秒,注塑 |
ASTMD2240 |
90 |
|
| 硬度 |
肖氏硬度 |
邵氏A,5秒,注塑 |
ASTMD2240 |
88 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-50.0 |
°C |
| 老化 |
ChangeinTensileStrengthinAir(158°C,168hr) |
|
ASTMD573 |
27 |
% |
| 老化 |
ChangeinUltimateElongationinAir(158°C,168hr) |
|
ASTMD573 |
-7.0 |
% |
| 老化 |
ChangeinTensileStrength(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-4.0 |
% |
| 老化 |
ChangeinUltimateElongation(60°C,168hr,inIRM902Oil) |
|
ASTMD471 |
-4.0 |
% |
| 电气性能 |
体积电阻率 |
23°C |
ASTMD257 |
1.7E+16 |
ohms·cm |
| 电气性能 |
体积电阻率 |
50°C |
ASTMD257 |
5.3E+14 |
ohms·cm |
| 电气性能 |
介电强度(23°C) |
|
ASTMD149 |
43 |
kV/mm |
| 电气性能 |
介电常数 |
23°C,1MHz |
ASTMD150 |
2.53 |
|
| 电气性能 |
介电常数 |
23°C,1kHz |
ASTMD150 |
2.61 |
|
| 电气性能 |
耗散因数 |
23°C,1MHz |
ASTMD150 |
5.8E-3 |
|
| 电气性能 |
耗散因数 |
23°C,1kHz |
ASTMD150 |
5.8E-3 |
|
| 可燃性 |
FlameRating(1.5mm,NT,BK,WT) |
|
UL94 |
V-0 |
|
| 可燃性 |
极限氧指数 |
|
ASTMD2863 |
28 |
% |