| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.20to1.24 |
g/cm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
抗张强度 |
1.02mm |
ASTMD412 |
16.5 |
MPa |
| ELASTOMERS |
抗张强度 |
1.91mm |
ASTMD412 |
15.2 |
MPa |
| ELASTOMERS |
伸长率 |
Break,1.91mm |
ASTMD412 |
340 |
% |
| ELASTOMERS |
伸长率 |
Break,1.02mm |
ASTMD412 |
320 |
% |
| 硬度 |
肖氏硬度 |
邵氏A |
ASTMD2240 |
78to84 |
|
| 硬度 |
肖氏硬度 |
邵氏A,15秒 |
ASTMD2240 |
68to74 |
|
| 热性能 |
脆化温度 |
|
ASTMD746 |
-49.0 |
°C |
| 热性能 |
Deformation-retention,1hour(150°C,1.27mm) |
|
|
58 |
% |
| 老化 |
ChangeinTensileStrengthinAir2(136°C,168hr) |
|
ULUnspecified |
0.0 |
% |
| 老化 |
空气中极限伸长率的变化率2(136°C,168hr) |
|
ULUnspecified |
-15 |
% |
| 老化 |
ChangeinTensileStrength2(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
0.0 |
% |
| 老化 |
ChangeinUltimateElongation2(60°C,168hr,inASTM#2Oil) |
|
ULUnspecified |
-10 |
% |