| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
|
ASTMD792 |
1.34 |
g/cm³ |
| 物理性能 |
Thickness-LayerCapability |
|
|
254.0到330.2 |
µm |
| 机械性能 |
拉伸模量3(3.18mm) |
|
ASTMD638 |
2220 |
MPa |
| 机械性能 |
抗张强度3(3.18mm) |
|
ASTMD638 |
71.7 |
MPa |
| 机械性能 |
伸长率3(断裂,3.18mm) |
|
ASTMD638 |
6.0 |
% |
| 机械性能 |
弯曲模量4 |
|
ASTMD790 |
2500 |
MPa |
| 机械性能 |
弯曲强度4 |
|
ASTMD790 |
115 |
MPa |
| 机械性能 |
压缩模量 |
|
ASTMD732 |
1930 |
MPa |
| 机械性能 |
压缩强度 |
|
ASTMD695 |
105 |
MPa |
| 机械性能 |
剪切强度(6.35mm) |
|
ASTMD732 |
57.2 |
MPa |
| 冲击性能 |
悬壁梁缺口冲击强度(23°C) |
|
ASTMD256A |
110 |
J/m |
| 冲击性能 |
无缺口悬臂梁冲击(23°C) |
|
ASTMD256 |
610 |
J/m |
| 热性能 |
载荷下热变形温度(1.8MPa,未退火,3.18mm) |
|
ASTMD648 |
153 |
°C |
| 热性能 |
玻璃转化温度 |
|
DSC |
367 |
°C |
| 热性能 |
线形热膨胀系数-流动 |
|
ASTME228 |
6.6E-5 |
cm/cm/°C |
| 电气性能 |
介电强度5,6 |
|
ASTMD149 |
4.3到11 |
kV/mm |
| 电气性能 |
介电常数6 |
|
ASTMD150 |
3.00到3.20 |
|
| 电气性能 |
耗散因数6 |
|
ASTMD150 |
2.6E-3到2.7E-3 |
|
| 电气性能 |
VolumeResistance6 |
|
ASTMD257 |
6.0E+13到1.0E+14 |
ohms |
| 可燃性 |
UL阻燃等级 |
|
UL94 |
V-0 |
|
| 可燃性 |
NBSSmokeDensity |
flaming |
ASTMF814/E662 |
Passed |
|
| 可燃性 |
NBSSmokeDensity |
non-flaming |
ASTMF814/E662 |
Passed |
|
| 可燃性 |
OSU总放热量 |
2mintest |
FAR25.853 |
16.0 |
kW·min/m² |
| 可燃性 |
OSU总放热量 |
5mintest |
FAR25.853 |
36.0 |
kW/m² |
| 可燃性 |
垂直燃烧-60秒(1.02到6.35mm) |
|
FAR25.853 |
2.0 |
sec |
| 可燃性 |
放热-65/65,<40HRPeak(1.52mm) |
|
FAR25.853 |
Passed |
|
| 可燃性 |
可燃性-FAA |
|
FAR25.853 |
<5.00 |
|
| 可燃性 |
UL阻燃等级 |
|
UL94 |
V-0 |
|
| 可燃性 |
NBSSmokeDensity |
flaming |
ASTMF814/E662 |
Passed |
|
| 可燃性 |
NBSSmokeDensity |
non-flaming |
ASTMF814/E662 |
Passed |
|
| 可燃性 |
OSU总放热量 |
2mintest |
FAR25.853 |
16.0 |
kW·min/m² |
| 可燃性 |
OSU总放热量 |
5mintest |
FAR25.853 |
36.0 |
kW/m² |
| 可燃性 |
垂直燃烧-60秒(1.02到6.35mm) |
|
FAR25.853 |
2.0 |
sec |
| 可燃性 |
放热-65/65,<40HRPeak(1.52mm) |
|
FAR25.853 |
Passed |
|
| 可燃性 |
可燃性-FAA |
|
FAR25.853 |
<5.00 |
|
| 补充信息 |
Outgassing |
CollectedVolatileCondensableMaterial(CVCM) |
ASTME595 |
-0.10 |
% |
| 补充信息 |
Outgassing |
TotalMassLost(TML) |
ASTME595 |
0.41 |
% |
| 补充信息 |
Outgassing |
WaterVaporRecovered(WVR) |
ASTME595 |
-0.37 |
% |
| 补充信息 |
抗真菌性-Method508.6 |
|
MILSTD-810G |
Passed |
|