| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.21 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53479 |
1.20 |
g/cm³ |
| 物理性能 |
MeltVolume-FlowRate(MVR)(190°C/10.0kg) |
|
|
60.0 |
cm³/10min |
| 物理性能 |
收缩率-流动(注塑) |
|
ASTMD955 |
0.40 |
% |
| 机械性能 |
Abrasion2 |
|
DIN53516 |
20 |
mm³ |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
ASTMD412 |
4.69 |
MPa |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
DIN53504 |
8.50 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
ASTMD412 |
10.3 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
DIN53504 |
16.0 |
MPa |
| ELASTOMERS |
TensileStrength3(Break,0.635mm) |
|
ASTMD412 |
37.9 |
MPa |
| ELASTOMERS |
TensileStress3(Break,0.635mm) |
|
DIN53504 |
36.0 |
MPa |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
ASTMD412 |
570 |
% |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
DIN53504 |
600 |
% |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
ASTMD624 |
80.6 |
kN/m |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
DIN53515 |
83 |
kN/m |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
ASTMD395 |
25 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
ASTMD395 |
40 |
% |
| ELASTOMERS |
压缩永久变形2 |
23°C,24hr |
DIN53517 |
25 |
% |
| ELASTOMERS |
压缩永久变形2 |
70°C,24hr |
DIN53517 |
0.40 |
% |
| ELASTOMERS |
压缩永久变形2 |
巴肖氏弹性 |
DIN53517 |
1 |
% |
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
ASTMD2240 |
90 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
ASTMD2240 |
38 |
|
| 硬度 |
肖氏硬度 |
邵氏A,注塑 |
DIN53505 |
90 |
|
| 硬度 |
肖氏硬度 |
邵氏D,注塑 |
DIN53505 |
38 |
|
| 热性能 |
TMA2 |
High |
InternalMethod |
170 |
°C |
| 热性能 |
TMA2 |
Low |
InternalMethod |
125 |
°C |