| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重2 |
|
ASTMD792 |
1.15 |
g/cm³ |
| 物理性能 |
密度3 |
|
DIN53478 |
1.15 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/5.0kg) |
|
|
59 |
g/10min |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
ASTMD412 |
5.45 |
MPa |
| ELASTOMERS |
TensileStress3(100%Strain,0.635mm) |
|
DIN53504 |
3.00 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
ASTMD412 |
6.27 |
MPa |
| ELASTOMERS |
TensileStress3(300%Strain,0.635mm) |
|
DIN53504 |
4.00 |
MPa |
| ELASTOMERS |
TensileStrength3(Break,0.635mm) |
|
ASTMD412 |
10.0 |
MPa |
| ELASTOMERS |
TensileStress3(Break,0.635mm) |
|
DIN53504 |
17.2 |
MPa |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
ASTMD412 |
650 |
% |
| ELASTOMERS |
TensileElongation3(Break,0.635mm) |
|
DIN53504 |
600 |
% |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
ASTMD624 |
80.6 |
kN/m |
| ELASTOMERS |
TearStrength3(0.635mm) |
|
DIN53515 |
110 |
kN/m |
| 硬度 |
肖氏硬度(邵氏A,注塑) |
|
ASTMD2240 |
95 |
|
| 硬度 |
ShoreHardness(ShoreA,InjectionMolded) |
|
DIN53505 |
95 |
|
| 热性能 |
熔融温度 |
|
InternalMethod |
80.0to110 |
°C |