ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 良好的耐候性、高耐冲击 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 7.0 | g/10min |
| 熔体流动速率 | 260℃/5.0kg | ASTM D-1238 | 13 | g/10min | |
| 吸水率 | Equilibrium，23℃ | ASTM D-570 | 0.55 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.06 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 1790 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 41.4 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 34.5 | MPa | ||
| 拉伸断裂伸长率 | ASTM D-638 | 40 | % | ||
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 1790 | MPa | |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 58.6 | MPa | |
| IZOD缺口冲击强度 | -30℃ | ASTM D-256 | 58.7 | J/m | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 320 | J/m | |
| 洛氏硬度 | ASTM D-785 | 86 | R scale | ||
| 电气性能 | 表面电阻率 | ASTM D-257 | >1.0E+15 | ohms | |
| 介电强度 | 3.20mm,in Oil | ASTM D-149 | 16.0 | KV/mm | |
| 介电常数 | 50Hz | ASTM D-150 | 5.200 | ||
| 介电常数 | 60Hz | ASTM D-150 | 5.200 | ||
| 介电常数 | 1E+6Hz | ASTM D-150 | 3.210 | ||
| 介电损耗因数 | 50Hz | ASTM D-150 | 0.15 | ||
| 介电损耗因数 | 60Hz | ASTM D-150 | 0.15 | ||
| 介电损耗因数 | 1E+6Hz | ASTM D-150 | 0.26 | ||
| 热性能 | 热变形温度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 87.8 | ℃ |
| 热变形温度 | 0.45MPa，未退火，6.40mm | ASTM D-648 | 90.6 | ℃ | |
| 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 76.7 | ℃ | |
| 热变形温度 | 1.80MPa，未退火，6.40mm | ASTM D-648 | 79.4 | ℃ | |
| 热变形温度 | 1.80MPa，退火 | ASTM D-648 | 95.6 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 99.4 | ℃ | ||
| CLTE | Flow,-30 TO 0℃ | ASTM E-831 | 0.000085 | cm/cm/℃ | |
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.000086 | cm/cm/℃ | |
| CLTE | Flow,0TO100℃ | ASTM E-831 | 0.000090 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.000092 | cm/cm/℃ | |
| 燃烧性 | 1.50mm | UL 94 | HB | ||
| RTI Str | UL 746 | 50.0 | ℃ | ||
| RTI Imp | UL 746 | 50.0 | ℃ | ||
| RTI Elec | UL 746 | 50.0 | ℃ | ||