ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 挤出 | 外观颜色 | |
| 该料用途 | |||
| 备注说明 | 光泽度低 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 220℃/10.0kg | ASTM D-1238 | 7.0 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.07 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.50-0.70 | % | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 2070 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 41.4 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 31.7 | MPa | ||
| 拉伸屈服伸长率 | ASTM D-638 | 3.0 | % | ||
| 拉伸断裂伸长率 | ASTM D-638 | 24 | % | ||
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 2070 | MPa | |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 62.1 | MPa | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 288 | J/m | |
| 洛氏硬度 | ASTM D-785 | 95 | R scale | ||
| 热性能 | 热变形温度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 87.8 | ℃ |
| 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 78.9 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 99.4 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 8.6 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 9.2 | cm/cm/℃ | |