ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 其它 其它 吹塑 | 外观颜色 | |
| 该料用途 | 吹塑应用、薄片 | ||
| 备注说明 | 高耐冲击 | ||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体体积流率 | 220℃/10.0kg | ASTM D-1238 | 4.00 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.03 | g/cm3 | |
| 模具收缩率 | Flow,3.20mm | ASTM D-955 | 0.70-0.90 | % | |
| 机械性能 | 拉伸模量 | ASTM D-638 | 1680 | MPa | |
| 拉伸屈服强度 | ASTM D-638 | 35.9 | MPa | ||
| 拉伸断裂强度 | ASTM D-638 | 29.0 | MPa | ||
| 拉伸屈服伸长率 | ASTM D-638 | 3.5 | % | ||
| 拉伸断裂伸长率 | ASTM D-638 | 110 | % | ||
| 弯曲模量 | 50.0mm Span | ASTM D-790 | 1900 | MPa | |
| 弯曲屈服强度 | 50.0mm Span | ASTM D-790 | 57.9 | MPa | |
| IZOD缺口冲击强度 | -30℃ | ASTM D-256 | 320 | J/m | |
| IZOD缺口冲击强度 | 23℃ | ASTM D-256 | 465 | J/m | |
| 热性能 | 热变形温度 | 0.45MPa，未退火，3.20mm | ASTM D-648 | 91.7 | ℃ |
| 热变形温度 | 1.80MPa，未退火，3.20mm | ASTM D-648 | 77.8 | ℃ | |
| 维卡软化温度 | ASTM D-1525 | 95.0 | ℃ | ||
| CLTE | Flow,-40TO40℃ | ASTM E-831 | 0.00010 | cm/cm/℃ | |
| CLTE | Transverse,-40TO40℃ | ASTM E-831 | 0.00012 | cm/cm/℃ | |
| 燃烧性 | 1.52mm | UL 94 | HB | ||