| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.919 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
3.7 |
g/10min |
| 薄膜 |
SecantModulus-MD(22µm,CastFilm) |
|
ASTMD882 |
117 |
MPa |
| 薄膜 |
SecantModulus-TD(22µm,CastFilm) |
|
ASTMD882 |
112 |
MPa |
| 薄膜 |
TensileStrength-MD(Break,22µm,CastFilm) |
|
ASTMD882 |
45.1 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,22µm,CastFilm) |
|
ASTMD882 |
38.2 |
MPa |
| 薄膜 |
TensileElongation-MD(Break,22µm,CastFilm) |
|
ASTMD882 |
450 |
% |
| 薄膜 |
TensileElongation-TD(Break,22µm,CastFilm) |
|
ASTMD882 |
600 |
% |
| 薄膜 |
DartDropImpact(22µm,CastFilm) |
|
ASTMD1709A |
500 |
g |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
107 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
116 |
°C |
| 光学性能 |
Haze(22.0µm,CastFilm) |
|
ASTMD1003 |
0.50 |
% |