| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
密度 |
|
ASTMD1505 |
0.924 |
g/cm³ |
| 物理性能 |
熔流率（熔体流动速率）(190°C/2.16kg) |
|
ASTMD1238 |
1.2 |
g/10min |
| 薄膜 |
TensileStrength-MD(Break,30µm,BlownFilm) |
|
ASTMD882 |
60.8 |
MPa |
| 薄膜 |
TensileStrength-TD(Break,30µm,BlownFilm) |
|
ASTMD882 |
49.0 |
MPa |
| 薄膜 |
伸长率-MD(断裂,30µm,吹塑薄膜) |
|
ASTMD882 |
530 |
% |
| 薄膜 |
TensileElongation-TD(Break,30µm,BlownFilm) |
|
ASTMD882 |
570 |
% |
| 薄膜 |
落锤冲击(30µm,吹塑薄膜) |
|
ASTMD1709A |
130 |
g |
| ELASTOMERS |
弹性体 |
|
TestMethod |
NominalValue |
Unit |
| ELASTOMERS |
撕裂强度 |
横向流量:0.0300mm |
ASTMD1004 |
132 |
kN/m |
| ELASTOMERS |
撕裂强度 |
流量:0.0300mm |
ASTMD1004 |
127 |
kN/m |
| 热性能 |
维卡软化温度 |
|
ASTMD1525 |
109 |
°C |
| 热性能 |
熔融峰值温度 |
|
ASTMD3418 |
117 |
°C |
| 光学性能 |
光泽度(45°,30.0µm,吹塑薄膜) |
|
ASTMD2457 |
89 |
|
| 光学性能 |
雾度(30.0µm,吹塑薄膜) |
|
ASTMD1003 |
20 |
% |