ABS A310 北京[分类 牌号 厂家] 中间用空格键
| 规格级别 | 己烯共聚单体,高 ESCR（抗应力开裂）,高分子量,良好的熔体强度,食品接触的合规性,可加工性，良好 挤出 | 外观颜色 | |
| 该料用途 | 管件 | ||
| 备注说明 | |||
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| Physical | 密度 | ASTMD1505 | 0.937 | g/cm³ | |
| Physical | 熔流率（熔体流动速率）(190°C/2.16kg) | ASTMD1238 | 0.28 | g/10min | |
| Physical | 抗环境应力开裂 | 10%Igepal,模压成型,F50 | ASTMD1693B | >2000 | hr |
| Physical | 抗环境应力开裂 | 100%Igepal,模压成型,F50 | ASTMD1693C | >2000 | hr |
| Physical | SP-NCTL | ASTMD5397 | >1.4 | month | |
| Mechanical | 抗张强度3(屈服,模压成型) | ASTMD638 | 19.0 | MPa | |
| Mechanical | 伸长率3(断裂,模压成型) | ASTMD638 | 750 | % | |
| Mechanical | FlexuralModulus-Tangent4(CompressionMolded) | ASTMD790 | 790 | MPa | |
| Impact | TensileImpactStrength5(CompressionMolded) | ASTMD1822 | 420 | kJ/m² | |
| Hardness | 肖氏硬度(邵氏D,模压成型) | ASTMD2240 | 60 | ||
| Thermal | 载荷下热变形温度(0.45MPa,未退火,模压成型) | ASTMD648 | 57.0 | °C | |
| Thermal | 脆化温度 | ASTMD746A | <-75.0 | °C | |
| Thermal | 维卡软化温度 | ASTMD15256 | 117 | °C | |